    A simple inorganic modifier for acrylic emulsions used to produce hybrid films with minimal aggregation of silica nanoparticles

    • Last Update: 2020-11-08
    • Source: Internet
    • Author: User
    Search more information of high quality chemicals, good prices and reliable suppliers, visit www.echemi.com
    Prepare the mixed lotion by mixing PreEm with AcEm. The emulsion obtains a transparent coating film with a high silicon dioxide content. As the content of silicon dioxide increases, the hardness of the film increases

    .
    with the help of an ionic surfactant with a low turbidity point (T cp - 40 degrees C), a new nanocomposite emulsion consisting of collide silica particles covered with a thin coating of polyacrylate (PreEm) has been successfully prepared. The non-ion surfactant is first deposited on the surface of the collome silica particles higher than its T cp to provide adsorption points and subsequent polymerization of the acrylic monosome.
    the scanning transmission electron microscope of the collome particles obtained after polymerization indicates the presence of a very thin polyacrylate coating (thickness of approximately 1-3nm nm) around the silicon dioxide nanoparticles. These PreEm particles are easily mixed into ordinary acrylic emulsions (AcEm) for silicon dioxide/polyacrylate blends (PreEm / AcEm).
    mixing emulsion can obtain a transparent coating film
    the results show that the mixed emulsion can obtain a transparent coating film at a ratio of less than 150/100 silica/polyacrylate, where collome particles are distributed in the polymer substrate without aggregation. This pattern contrasts sharply with the particle aggregation pattern shown by the exposed collome silicon dioxide-AcEm mixture emulsion and the film obtained from conventional nanocomposite emulsions covered with thick polyacrylate-coated silicon dioxide particles.
    content of preEm/AcEm membranes increases to 150% and hardness increases. These data support PreEm's effectiveness in controlling the performance of the silicon dioxide-polyacrylate blend film.
    the study has been published in Progress in Organic Coatings. Volume 128.
    This article is an English version of an article which is originally in the Chinese language on echemi.com and is provided for information purposes only. This website makes no representation or warranty of any kind, either expressed or implied, as to the accuracy, completeness ownership or reliability of the article or any translations thereof. If you have any concerns or complaints relating to the article, please send an email, providing a detailed description of the concern or complaint, to service@echemi.com. A staff member will contact you within 5 working days. Once verified, infringing content will be removed immediately.

    Contact Us

    The source of this page with content of products and services is from Internet, which doesn't represent ECHEMI's opinion. If you have any queries, please write to service@echemi.com. It will be replied within 5 days.

    Moreover, if you find any instances of plagiarism from the page, please send email to service@echemi.com with relevant evidence.