Coating classification: cathodic protection heavy-duty anticorrosive coating h06-4

Core tip: Introduction: cathodic protection heavy-duty anticorrosive coating h06-4 is a two-component or three-component epoxy zinc rich heavy-duty anticorrosive primer, which is composed of epoxy resin, ultra-fine powder and special additives, and is prepared by advanced technology with polyamide as curing agent When in use, mix according to the specified proportion, fully mix and use up within the specified time Features: the features of cathodic protection heavy-duty anticorrosive coating h06-4 are as follows: ① The coating performance of h06-4 is excellent; The coating of h06-4 has excellent cathodic protection effect Paint agent, top 10 Chinese wall paint brands Recommended introduction: interior wall paint and exterior wall paint can achieve beautiful, clean and pleasant effects, but the effects in different environments are different, so the color of the paint will be different There are ten brands of Chinese paint, ten brands of global paint, ten brands of Chinese wall paint, and ten brands of Chinese paint, Famous trademark of Chinese paint and coating In private rooms, most of us choose according to our own personality, personal hobbies and living habits The younger generation will choose the interior wall paint with rich colors and bright colors, while the older ones will have some working experience Introduction: cathodic protection heavy-duty anticorrosive coating h06-4 is a two-component or three-component epoxy zinc rich heavy-duty anticorrosive primer, which is composed of epoxy resin, ultra-fine powder and special additives, and is prepared by advanced technology with polyamide as curing agent When in use, mix according to the specified proportion, fully mix and use up within the specified time Features: the features of cathodic protection heavy-duty anticorrosive coating h06-4 are as follows: ① the coating performance of cathodic protection heavy-duty anticorrosive coating h06-4 is excellent; the coating of cathodic protection heavy-duty anticorrosive coating h06-4 has excellent cathodic protection, good conductivity, strong adhesion, weather resistance and durability ② Cathodic protection heavy-duty anticorrosive coating h06-4 is easy to use and can be cured at room temperature The construction process of cathodic protection heavy-duty anticorrosive coating h06-4 is simple, not limited by the site environment It can only be used when it is used, and it can be solidified into a film at room temperature by using general construction method The cathodic protection heavy-duty anticorrosive coating h06-4 has the characteristics of quick drying, tough film and strong adhesion It has excellent electrochemical protection, electrostatic conductivity and antirust performance It is not suitable to be used as the matching primer directly soaked with acid, alkali and other strong corrosive media, or directly coated with alkyd and other oil-based finish Technical parameters: see Table 1 for technical parameters of cathodic protection heavy-duty anticorrosive coating h06-4 Table 1 technical indicators of cathodic protection heavy-duty anticorrosive coating h06-4 technical indicators of the project technical indicators of the original paint state the paint base is a flowable slurry, the curing agent is the liquid paint film color and appearance gray, the paint film is flat, no visible particles drying time / h surface drying ≤ 0.5 solid drying ≤ 24 adhesion / grade ≤ 2 flexibility / mm ≤ 1 impact strength / (kg · cm) 50 Salt water resistance (coating two coats of paint, dry film 40 μ m, soaking in 3% salt water, 96 h) non foaming and non rusting construction matters: see Table 2 for construction matters of cathodic protection heavy-duty anticorrosive coating h06-4 Table 2 construction items of cathodic protection heavy-duty anticorrosive coating h 0 6-4 deployment weight ratio paint base: curing agent = 9:1 service life after mixing / h 6 density after mixing / (kg / L) 2.3 flash point / ℃ 27 film thickness of each paint / μ m dry film 20 wet film 45 theoretical paint consumption (dry film 20 μ m) 0.11 kg / m2 recommended one coat (as maintenance primer); two coats (as antirust paint) The interval time of recoating / h 16 The surface treatment of steel after coating must be sandblasted to Sa2.5 according to the needs The surface roughness is 30-70 μ M the temperature of the coating in the construction environment is higher than 3 ℃ above the dew point, and the relative humidity is below 85% It is not suitable for the construction in rainy and snowy days and the temperature is below 5 ℃ Air spraying, airless spraying and small area repair can be brushed Transportation and storage: cathodic protection heavy-duty anticorrosive coating h06-4 shall be transported according to the National Transportation Regulations for hazardous chemicals and inflammables Store in a cool and ventilated warehouse away from fire and heat source The period of validity is 12 months for paint and 10 months for curing agent The use site shall be well ventilated, no fireworks, welding and explosion-proof equipment shall be used Solvent or paint mist is harmful to the body, please wear qualified and effective labor protection articles Those with slight discomfort can rest for a while, and those with serious discomfort can be sent to a doctor for treatment in time Home of coatings is specialized in coatings, diatom mud, paint coating, coating technology, fire retardant coating news and coating, diatom mud, paint coating, coating technology, fire retardant coating decoration knowledge and decoration renderings,