Coating classification: dry film lubricating coating

Core tip: Introduction: dark green thermosetting acrylic coil coating belongs to water-based coating Coating formula: the coating formula of dark green thermosetting acrylic coil coating is shown in Table 1 Table 1 deep green thermosetting acrylic coil coatings composition, name, specification, type, quality, acrylic emulsion Rhoplex-1230, 47%726.9 thickener Acrysol I-62, 25%320 DMAE50% aqueous solution 1.1 defoamer Foamaster TCX1.1 extinction agent Svl Application scope and advantages of roller ceramic coating Recommended introduction: the surface of ceramic rubber plate used for roller ceramic coating is cast into durable rubber plate by hundreds of independent small ceramic pieces Each ceramic piece has raised characteristics Under general conveyor belt pressure, thousands of unique cast bumps can produce positive traction, prevent slipping and extend the service life of conveyor belt roller At the same time, the bottom layer adopts high-quality rubber, which has strong elasticity and can play a good impact resistance role The scope of application of roller ceramic coating is one three six 83857180 (the same as V) 1 Roller coating in extremely harsh working environment 2 The belt joint is not suitable for fixing with iron buckle; 3 It is suitable for leather Introduction: dark green thermosetting acrylic coil coating belongs to water-based coating Coating formula: the coating formula of dark green thermosetting acrylic coil coating is shown in Table 1 Table 1 deep green thermosetting acrylic coatings composition, name, specification, type, quality, acrylic emulsion Rhoplex-1230, 47% 726.9 thickener Acrysol I-62, 25% 320 DMAE 50% water solution 1.1 defoamer Foamaster TCX 1.1 dull agent Svloid 7215.2 titanium dioxide R-960 82.6 green paste, 77.5 ethylene glycol mono butyl ether 77.5 water solution 77.5 976.2 in total for thickener or water 11.2 Table 2 ① name, specification and model of preparation components of green pulp quality fraction of phthalocyanine green gt-674 242.5 thickener acrysol i-62 48.5 dispersant Triton X-114 9.8 water 654.7 defoamer foamer TCX 3.7 preparation process: the total amount of 36 Acrylic acid emulsion, DMAE, defoamer, matting agent, green pulp and titanium dioxide were added to the paint mixing tank The mixture was evenly mixed The high speed dispersal was 20 min through the Coles kettle, then added ethylene glycol mono butyl ether, the remaining acrylic emulsion was mixed evenly, thickened agent or water was used to adjust the viscosity, and then filtered, packed and stored Main properties: dark green thermosetting acrylic coil coating is shown in Table 2 Table 3 main performance indexes of dark green thermosetting acrylic coil coating: solid content (mass) 48% pigment volume concentration 24% titanium dioxide / base material 25 / 75 purpose: dark green thermosetting acrylic coil coating is used for color coil coating Home of coatings is specialized in coatings, diatom mud, paint coating, coating technology, fire retardant coating news and coating, diatom mud, paint coating, coating technology, fire retardant coating decoration knowledge and decoration renderings,