Coating classification: polyaspartic ester coating

It is suggested that polyaspartic ester coating is a kind of coating with polyaspartic ester as base material and isocyanate as curing agent, which belongs to a kind of polyurea coating in essence When the curing agent is fatty acid isocyanate, it becomes a new type of high performance surface protective coating Polyaspartic ester can be directly constructed on the metal surface with standard construction equipment One layer of construction thickness is 150-250 microns (6-10 mils) When it is used in moderate corrosion environment (up to C3, iso12944-2), compared with two layers of paint, it can save construction time and labor cost gather Application scope and advantages of roller ceramic coating Recommended introduction: the surface of ceramic rubber plate used for roller ceramic coating is cast into durable rubber plate by hundreds of independent small ceramic pieces Each ceramic piece has raised characteristics Under general conveyor belt pressure, thousands of unique cast bumps can produce positive traction, prevent slipping and extend the service life of conveyor belt roller At the same time, the bottom layer adopts high-quality rubber, which has strong elasticity and can play a good impact resistance role The scope of application of roller ceramic coating is one three six 83857180 (the same as V) 1 Roller coating in extremely harsh working environment 2 The belt joint is not suitable for fixing with iron buckle; 3 It is suitable for leather Coating home news: polyaspartic ester coating is a kind of coating with polyaspartic ester as base material and isocyanate as curing agent, which is essentially a polyurea coating When the curing agent is fatty acid isocyanate, it becomes a new type of high performance surface protective coating Polyaspartic ester can be directly constructed on the metal surface with standard construction equipment One layer of construction thickness is 150-250 microns (6-10 mils) When it is used in moderate corrosion environment (up to C3, iso12944-2), compared with two layers of paint, it can save construction time and labor cost Polyaspartic acid ester is a kind of quick drying primer / finish with low VOC and high solid content, and it also provides excellent corrosion protection and long-term light and color retention performance, which can not be achieved by other quick drying and single primer paint substitutes Polyaspartic acid ester can also be used as a thick paste, durable intermediate paint / finish product, constructed on the approved anti-corrosion primer, and used in more severe corrosion environment, such as iso12944 C4 and C5 Polyaspartic acid ester is particularly suitable for use as a single coat of high performance topcoat As a steel structure construction, reducing the number of coating layers can help to improve production capacity and efficiency The features of quick drying and early handling make it very suitable for the occasions with high requirements for productivity and drying time, such as wind tower, transformer, mining equipment and pump Home of coatings is specialized in coatings, diatom mud, paint coating, coating technology, fire retardant coating news and coating, diatom mud, paint coating, coating technology, fire retardant coating decoration knowledge and decoration renderings,