Coating classification: vinyl acetate acrylic emulsion paint

Core tip: Introduction: vinyl acetate acrylic emulsion paint is vinyl acetate acrylic copolymer emulsion as the main film forming material emulsion paint Coating formula: the formula of vinyl acetate acrylic emulsion paint is shown in Table 1 Table 1 production formula, specification and quality of vinyl acetate acrylic emulsion paint 225 hydroxyethyl cellulose qp-520001 multifunctional assistant amp-953 dispersant daxad 306 potassium tripolyphosphate 0.5 glycol 20 bactericide 0.5 defoamer Application scope and advantages of roller ceramic coating Recommended introduction: the surface of ceramic rubber plate used for roller ceramic coating is cast into durable rubber plate by hundreds of independent small ceramic pieces Each ceramic piece has raised characteristics Under general conveyor belt pressure, thousands of unique cast bumps can produce positive traction, prevent slipping and extend the service life of conveyor belt roller At the same time, the bottom layer adopts high-quality rubber, which has strong elasticity and can play a good impact resistance role The scope of application of roller ceramic coating is one three six 83857180 (the same as V) 1 Roller coating in extremely harsh working environment 2 The belt joint is not suitable for fixing with iron buckle; 3 It is suitable for leather Paint Home News: Introduction: vinyl acetate acrylic emulsion paint is vinyl acetate acrylic copolymer emulsion as the main film forming material emulsion paint Coating formula: the formula of vinyl acetate acrylic emulsion paint is shown in Table 1 Table 1 specification and quality of production formula of vinyl acetate acrylic emulsion paint 225 hydroxyethyl cellulose qp-52000 1 multifunctional assistant amp-953 dispersant daxad 30 6 potassium tripolyphosphate 0.5 glycol 20 bactericide 0.5 defoamer 1 titanium dioxide 130 kaolin Huber 70c 100 calcium carbonate hubercarb Q6 60 sodium aluminosilicate zeolex 80 80 Cellulose solution more than 3 functional aids (pH regulator) AMP-95 3 ester alcohol -12 6 defoamer Nopco NDW 3 vinyl acetate acrylic copolymer emulsion 3011264 AMSOC 1086 preparation: 1086 deionized water, 1/4 hydroxyethyl cellulose, 1/2 polyenergetic auxiliaries and dispersant Daxad in measurement and order 30 Potassium tripolyphosphate, glycol, bactericide, 1 / 4 defoamer, titanium dioxide, kaolin, calcium carbonate, sodium aluminosilicate are added with high-speed dispersant for high-speed dispersion 20-30 After min, add residual deionized water, multifunctional auxiliary, hydroxyethyl cellulose and defoamer, ester alcohol -12, vinyl acetate acrylic acid copolymer emulsion at low speed stirring, stirring evenly, filtering, packing and storing Main properties of coating: see Table 2 for main properties of vinyl acetate acrylic emulsion paint Table 2 main performance indexes of vinyl acetate acrylic emulsion paint project performance indexes pigment volume concentration 51% viscosity 86 Ku covering power (black) 90.2 covering power (white) 92.3 contrast 0.977 scrub resistance (until failure) 800 decontamination (0-extremely poor, 10 excellent) 8 color matching excellent paint family is focused on coating, diatom mud, paint coating, Coating technology, fire retardant coating news and coating, diatom mud, paint coating, coating technology, decoration knowledge and decoration effect map of fire retardant coating,