Coating classification: waterborne inorganic zinc silicate primer coating

Core tip: brief introduction: the waterborne inorganic silicate zinc primer is a kind of thick paste waterborne zinc rich primer composed of modified inorganic silicate and zinc powder It belongs to the waterborne coating, and is a kind of anticorrosive coating with excellent performance It is mainly applicable to the anticorrosion of steel structures in marine environment and high temperature and humidity conditions Features: the characteristics of water-based inorganic zinc silicate primer coating are as follows: ① The waterborne inorganic zinc silicate primer has excellent gas cutting and welding properties; ② The waterborne inorganic zinc silicate primer can be matched with a variety of top coatings; ③ Water based inorganic zinc silicate primer has excellent long-term corrosion resistance Application scope and advantages of roller ceramic coating Recommended introduction: the surface of ceramic rubber plate used for roller ceramic coating is cast into durable rubber plate by hundreds of independent small ceramic pieces Each ceramic piece has raised characteristics Under general conveyor belt pressure, thousands of unique cast bumps can produce positive traction, prevent slipping and extend the service life of conveyor belt roller At the same time, the bottom layer adopts high-quality rubber, which has strong elasticity and can play a good impact resistance role The scope of application of roller ceramic coating is one three six 83857180 (the same as V) 1 Roller coating in extremely harsh working environment 2 The belt joint is not suitable for fixing with iron buckle; 3 It is suitable for leather Introduction: waterborne inorganic zinc silicate primer is a kind of thick paste water-based zinc rich primer composed of modified inorganic silicate and zinc powder It belongs to water-based coating and is an excellent anticorrosive coating It is mainly used for anticorrosion of steel structure components in marine environment and high temperature and humidity conditions Features: the characteristics of the waterborne inorganic zinc silicate primer are as follows: ① the waterborne inorganic zinc silicate primer has excellent gas cutting and welding performance; ② the waterborne inorganic zinc silicate primer can be matched with a variety of upper coatings; ③ the waterborne inorganic zinc silicate primer has excellent long-term corrosion resistance; ④ The water-based inorganic zinc silicate primer has excellent wear resistance, heat resistance and buckling resistance Technical parameters: project technical index color gray luster flat light mixing ratio main agent: zinc powder = 3:7 solid content 67 ± 1 specific gravity about 3.01 flash point / ℃ 9 film thickness dry film / μ m 30-50 wet film / μ m 45-74 coating rate theoretical coating rate 13.4 m2 / L actual coating rate and surface treatment, external environment, construction method and other factors related storage temperature: 5-40 ℃ Storage period: no less than 6 months, coating house is specialized in coating, diatom mud, paint coating, coating process, news information and coating of fireproof coating, diatom mud, paint coating, coating process, decoration knowledge and decoration effect map of fireproof coating,