Coating formula: a new type of intumescent facing fireproof coating formula

Key tips: 1 Formulation of new intumescent facing fire retardant coating: Raw material quality /kg ammonium polyphosphate 20 pentaerythritol 10 melamine 8 titanium white 4.2 4.2 expandable graphite 4 silicone acrylate emulsion 20 epoxy emulsion 20 acrylic emulsion 20 ethylene glycol 20 wetting dispersant, proper defoamer, proper mildew inhibitor, proper amount of film builder, 2, and preparation of fire retardant coating (1) Add water, dehydration catalyst, carbon forming agent, foaming agent, titanium dioxide and various additives to the grinder for 2h according to the formula proportion Paint knowledge how about Akzo Nobel Powder Coating Recommended introduction: powder coating is a kind of coating with different form from general coating, which is in powder form It is a new type of coating, because of its own advantages and more and more known by people Let's introduce Akzo Nobel Powder coating Akzo Nobel Powder coating is a cost-effective coating solution, which can be applied to different kinds of products After the treatment of static electricity and fire baking, a tough and durable coating surface will be formed, with the least impact on the environment Since the introduction of this technology, powder coating has been able to continue to maintain the Coatings home news: 1, the new type of expansive decorative fire retardant coating formula: raw material quality /kg ammonium polyphosphate 20 pentaerythritol 10 melamine 8 titanium white powder 4.2 expandable graphite 4 silicon acrylic emulsion 20 epoxy emulsion 20 acrylic emulsion 20 20 glycol 20 wetting dispersant proper defoaming agent, proper amount of mildew inhibitor, proper amount of film forming AIDS 2 Preparation of fire retardant coating: (1) add water, dehydration catalyst, carbon forming agent, foaming agent, titanium dioxide and various auxiliaries to the grinding machine for 2h according to the formula proportion (2) adding expandable graphite and hollow microspheres into the slurry, stirring 20min at a speed of 800 to 1000r/min, and then reducing the rotational speed to 200 ~ 400r/min, adding emulsion and other auxiliaries (3) Adjust the viscosity of the slurry system with water or thickener, and adjust the pH value to about 7.5 with ammonia water (the paint formula in this paper is for reference only) paint home is focused on the news and information of coating, diatom mud, paint coating, coating process, fire retardant coating, and coating, diatom mud, paint coating, coating process, decoration knowledge and decoration effect map of fire retardant coating,