Coating formula: water-based full shielding infrared and ultraviolet self-cleaning nano transparent thermal insulation coating formula

The key points are as follows: the formulation of a kind of water-based full shielding infrared and ultraviolet self-cleaning nano transparent thermal insulation coating, which includes film-forming resin 30% - 70%, nano ATO dispersion 5% - 30%, nano LaB6 dispersion 1% - 10%, nano WO3 dispersion 1% - 15%, cosolvent 5% - 15%, film-forming assistant 2% - 10%, assistant 0.5% - 5.0%, deionized water 5% - 25% The preparation method is: adding nano ATO dispersion, nano LaB6 dispersion and nano WO3 dispersion into the water-based fluorocarbon resin under stirring for 30 m Paint agent, top 10 Chinese wall paint brands Recommended introduction: interior wall paint and exterior wall paint can achieve beautiful, clean and pleasant effects, but the effects in different environments are different, so the color of the paint will be different There are ten brands of Chinese paint, ten brands of global paint, ten brands of Chinese wall paint, and ten brands of Chinese paint, Famous trademark of Chinese paint and coating In private rooms, most of us choose according to our own personality, personal hobbies and living habits The younger generation will choose the interior wall paint with rich colors and bright colors, while the older ones will have some working experience Coating House News: a kind of formulation of water-based fully shielded infrared and ultraviolet self-cleaning nano transparent thermal insulation coating, its components include film-forming resin 30% - 70%, nano ATO dispersion 5% - 30%, nano LaB6 dispersion 1% - 10%, nano WO3 dispersion 1% - 15%, cosolvent 5% - 15%, film-forming assistant 2% - 10%, assistant 0.5% - 5.0%, deionized water 5% - 25% The preparation method is: adding nano ATO dispersion, nano LaB6 dispersion and nano WO3 dispersion into the water-based fluorocarbon resin under stirring, stirring for 30min-40min, adding defoamer, wetting agent, film-forming assistant, thickener and accelerator in turn, stirring to obtain self-cleaning nano transparent and heat insulation coating The coating is used on the surface of building glass, vehicle glass and cement It has the function of self-cleaning, full shielding of ultraviolet, infrared and heat insulation Its specific formula is composed of water fluorocarbon emulsion 50%, nano ATO dispersion 20%, nano LaB6 dispersion 3%, nano WO3 dispersion 7%, dispersant 2%, defoamer 0.3%, substrate wetting agent 1.5%, film builder 2.5%, thickener 0.6%, thickener 1%, pH harmonic agent 0.5% and deionization Water 11.6%; wherein, nano ATO dispersion selects nano ATO slurry with a median particle size of 40nm-80nm and a solid content of 25%; nano LaB6 dispersion selects nano LaB6 slurry with a median particle size of 40nm-80nm and a solid content of 25%; nano WO3 dispersion selects nano WO3 slurry with a median particle size of 40nm-80nm and a solid content of 25% Home of coatings is specialized in coatings, diatom mud, paint coating, coating technology, fire retardant coating news and coating, diatom mud, paint coating, coating technology, fire retardant coating decoration knowledge and decoration renderings,