    Coating formulation: emulsion expansion fire retardant coating formulation

    • Last Update: 2020-04-03
    • Source: Internet
    • Author: User
    Search more information of high quality chemicals, good prices and reliable suppliers, visit www.echemi.com
    Core tip: emulsion expansion fire retardant coating formulation: ingredient dosage / mass fraction base material (ball mill): water 35 tripolyphosphate 0.3 polyphosphate ammonium 18 melamine 7, two pentaerythritol 7 chlorinated paraffin 3 titanium white 3 additives (stirring): hydroxyethyl cellulose 5 ethylene acetate emulsion 25 defoamer 0.1 Process and performance modulation process are similar to general latex coating, mainly including the following steps: ① Preparation of auxiliary solution and pigment paste; ② Grinding and dispersing fire-proof slurry by sand mill or ball mill; Electricity Application scope and advantages of roller ceramic coating Recommended introduction: the surface of ceramic rubber plate used for roller ceramic coating is cast into durable rubber plate by hundreds of independent small ceramic pieces

    Each ceramic piece has raised characteristics

    Under general conveyor belt pressure, thousands of unique cast bumps can produce positive traction, prevent slipping and extend the service life of conveyor belt roller

    At the same time, the bottom layer adopts high-quality rubber, which has strong elasticity and can play a good impact resistance role

    The scope of application of roller ceramic coating is one three six 83857180 (the same as V) 1

    Roller coating in extremely harsh working environment 2

    The belt joint is not suitable for fixing with iron buckle; 3

    It is suitable for leather Coatings home news: emulsion expansion fire retardant coating formulation: ingredient dosage / mass fraction base material (ball mill): water 35 tripolyphosphate 0.3 polyphosphate ammonium 18 melamine 7, two pentaerythritol 7 chlorinated paraffin, 3 titanium white, 3 after additives (stirring): hydroxyethyl cellulose 5 ethylene acetate emulsion 25 defoamer 0.1 The process and performance modulation process are similar to the general latex coating, mainly including the following steps: ① preparation of auxiliary solution and coloring pigment slurry; ② grinding and dispersing of fireproof slurry by sand mill or ball mill; ③ preparation of fireproof coating by electric mixer; ④ inspection of packaging

    (the paint formula in this paper is for reference only) paint home is focused on the news and information of coating, diatom mud, paint coating, coating process, fire retardant coating, and coating, diatom mud, paint coating, coating process, decoration knowledge and decoration effect map of fire retardant coating,
    This article is an English version of an article which is originally in the Chinese language on echemi.com and is provided for information purposes only. This website makes no representation or warranty of any kind, either expressed or implied, as to the accuracy, completeness ownership or reliability of the article or any translations thereof. If you have any concerns or complaints relating to the article, please send an email, providing a detailed description of the concern or complaint, to service@echemi.com. A staff member will contact you within 5 working days. Once verified, infringing content will be removed immediately.
    Related Articles

    Contact Us

    The source of this page with content of products and services is from Internet, which doesn't represent Echemi's opinion. If you have any queries, please write to service@echemi.com. It will be replied within 5 days.

    Moreover, if you find any instances of plagiarism from the page, please send email to service@echemi.com with relevant evidence.