Coating formulation: pure acrylic emulsion formula for coating base material

Core tip: pure acrylic emulsion is mainly used for exterior wall latex paint, various color coatings The formula of pure acrylic emulsion for coating material is as follows: table{border-collapse:collapse; } table,td{ border: 1px solid #ccc; }Methyl methacrylate 208kg butyl acrylate 178kg methacrylate 7kg aminoacrylate 7kg anionic emulsifier 2kg nonylphenol ethoxylate 5kg reactive emulsifier 1kg carbon Paint knowledge how about Akzo Nobel Powder Coating Recommended introduction: powder coating is a kind of coating with different form from general coating, which is in powder form It is a new type of coating, because of its own advantages and more and more known by people Let's introduce Akzo Nobel Powder coating Akzo Nobel Powder coating is a cost-effective coating solution, which can be applied to different kinds of products After the treatment of static electricity and fire baking, a tough and durable coating surface will be formed, with the least impact on the environment Since the introduction of this technology, powder coating has been able to continue to maintain the Paint Home News: pure acrylic emulsion is mainly used for exterior wall latex paint, all kinds of color coatings The formulation of pure acrylic emulsion for coating materials is as follows: table{border-collapse:collapse;} table, td{border: 1px solid #ccc;} methyl methacrylate, 208kg butyl acrylate, 178kg methacrylic acid 7kg amino acrylic ester 7kg anionic emulsifier, nonylphenol polyoxyethylene ether, emulsifier, sodium bicarbonate (regulator) potassium persulfate (initiator) Deionized water 400kg is used to prepare emulsion in 1000L enamel reactor with stirrer, condenser and thermometer Firstly, some emulsifiers, water and monomers are added into the emulsifier for pre emulsification, and then the remaining emulsifiers are added into the reactor At a certain temperature, 10% of the pre emulsified monomers and 30% of the initiator solution are added for seed polymerization The remaining pre emulsified monomer and initiator solution were added to the reactor in 3 hours, and the temperature was controlled at 82 ~ 84 ℃ Heat preservation for 1h after feeding After cooling to 65 ℃, add redox agent to eliminate, continue to react for 0.5h, finally cool to below 40 ℃, neutralize with dispersant amp ~ 95 to pH = 7 ~ 8, and then filter to obtain the finished product Home of coatings is specialized in coatings, diatom mud, paint coating, coating technology, fire retardant coating news and coating, diatom mud, paint coating, coating technology, fire retardant coating decoration knowledge and decoration renderings,