Coating process: coating process of forklift structure

Core tip: the standard requirements for forklift structure parts: medium paint, average film thickness of 30 μ m; finish paint, average film thickness of 59 μ M The structural parts and counterweights of forklift trucks are generally coated with environmental primer + two-component acrylic polyurethane finish; while the sheet metal parts are coated with phosphating, powder spraying, or cathodic electrophoretic paint + high temperature wet touch finish In the design of coating process, shot blasting of structural parts, putty polishing after primer and pickling of sheet metal hot rolled parts shall be considered See the following table: No process name processing method process temperature / ℃ process time / mi Shenyang steel structure fireproof coating construction expert punde Building Fire Engineering Co., Ltd Recommended introduction: since its establishment, Shenyang punde Construction Fire Engineering Co., Ltd has cultivated a group of professional construction teams with excellent equipment, rich experience and serious responsibility with advanced and scientific management methods and strict engineering quality assurance and after-sales service system It has undertaken a number of fire system installation projects, which has been praised by customers Every idea and special requirement of you will be fully considered by us and fully realized in the construction technology, which will become the cornerstone of our successful long-term development We are looking forward to your invitation, to provide you with quality services and high-quality technical support! All construction coatings have passed ISO9001 Home of coatings: standard requirements for forklift structural parts: medium paint, average film thickness of 30 μ m; finish paint, average film thickness of 59 μ M The structural parts and counterweights of forklift trucks are generally coated with environmental primer + two-component acrylic polyurethane finish; while the sheet metal parts are coated with phosphating, powder spraying, or cathodic electrophoretic paint + high temperature wet touch finish In the design of coating process, shot blasting of structural parts, putty polishing after primer and pickling of sheet metal hot rolled parts shall be considered, as shown in the following table: No process name processing method process temperature / ℃ process time / Min1 on-line manual assistance 2 shot blasting, soot blowing cleaning automatic room temperature 3 primer spraying manual room temperature ~ 54 primer leveling, air drying room temperature ~ 105 putty scraping manual room temperature ~ 106 putty drying hot air circulation 60 ~ 80 ~ 207 putty strong cold air cooling room temperature ~ 108 putty grinding, cleaning manual room temperature ~ 209 paint spraying manual room temperature ~ 510 paint leveling room temperature ~ 1011 Middle painting drying hot air circulation 60 ~ 80 ~ 2012 middle painting strong cold air cooling room temperature ~ 1013 middle painting grinding artificial room temperature ~ 1014 middle painting soot blowing artificial room temperature ~ 515 top coating 1 Artificial room temperature ~ 516 top coating leveling 1 room temperature ~ 1017 top coating 2 artificial room temperature ~ 518 top coating leveling 2 room temperature ~ 1019 top coating drying hot air circulation 60 ~ 80 ~ 4020 top coating strong cold line air cooling room temperature ~ 10 coating home is focused on coating, diatom mud, paint News and information of coatings, coating technology, fire retardant coatings, diatom mud, paint coatings, coating technology, decoration knowledge and decoration effect map of fire retardant coatings,