Coating process: metal anticorrosive waterborne coating -- the production process of acrylic emulsion liquid primer

Core tips: the production process: metal anticorrosive waterborne coatings - acrylic emulsion primer paint formula is shown in the table below Metal anticorrosive waterborne coatings -- formulation of acrylic emulsion Component name, specification, model, weight, water 165.00 hydroxyethyl cellulose, natrosol 1.73 defoamer, NOPCO nxz1.80 ammonia water 28%, 0.87 dispersant, tamol 850 (30%), 13.48 wetting agent, trition cf-102.12 titanium dioxide Paint knowledge how about Akzo Nobel Powder Coating Recommended introduction: powder coating is a kind of coating with different form from general coating, which is in powder form It is a new type of coating, because of its own advantages and more and more known by people Let's introduce Akzo Nobel Powder coating Akzo Nobel Powder coating is a cost-effective coating solution, which can be applied to different kinds of products After the treatment of static electricity and fire baking, a tough and durable coating surface will be formed, with the least impact on the environment Since the introduction of this technology, powder coating has been able to continue to maintain the Coating home: production process: metal anticorrosive waterborne coatings - acrylic emulsion primer paint formula is shown in the table below Metal anticorrosive waterborne coatings -- formulation of acrylic emulsion composition, name, specification, type, mass fraction, water 165 hydroxyethyl cellulose Natrosol 1.73 defoamer Nopco NXZ 1.80, ammonia 28% 0.87 dispersant Tamol 850 (30%) 13.48 wetting agent Trition CF-10 2.12 titanium dioxide Ti-Pure R-960 144.40 water grinding mica 325 mesh calcium carbonate Atomite Atomite barium borate Busan 11-M1 96.26 acrylic emulsion Rhoplex MV-2 (46%) 446.86 emulsifier Triton X-405 (70%) 1.64 alcohol ester -12 3.66 alkyd resin Aroplaz 1271 (1) 57.76 emulsifier Triton X-100 4.28 ethylene glycol 22.33 sodium nitrite solution 4.28% water / hydroxyethyl cellulose solution total amount of sulfur (the coating formulation is for reference only) The production process of metal anticorrosive waterborne coatings, acrylic emulsion primer, is as follows: Deionized water, hydroxyethyl cellulose and 1/2 defoamers are added to the dispersing kettle and mixed evenly; then ammonia, dispersant, wetting agent, titanium dioxide, water mica, calcium carbonate and barium borate are mixed evenly and dispersed at high speed by 20 Min to fineness qualified; then add acrylic emulsion (emulsifier Triton X-405 (70%) premixed), alcohol ester -12, alkyd resin (emulsifier Triton X-100 premixed), glycol, sodium nitrite solution, the remaining defoamer, mix evenly; finally add water or hydroxyethyl cellulose solution to adjust the viscosity to 65 KU, discharge, filter, packaging The drier of aroplaz 1271 is composed of 0.14 kg 6% cobalt drier, 0.14 kg 6% zirconium drier and 1.53 kg 6% manganese drier Home of coatings is specialized in coatings, diatom mud, paint coating, coating technology, fire retardant coating news and coating, diatom mud, paint coating, coating technology, fire retardant coating decoration knowledge and decoration renderings,