Coating process: production process of acrylic interior semi gloss latex enamel

Core tips: 1, acrylic semi gloss emulsion enamel formula: raw material /kg water 217.8 preservative 2.4 propylene glycol 25.9 dispersant 11.5 defoamer 3.8 surfactant 1 (Triton N-57) 12- amino -2- methyl -1- propanol 1 titanium white 250 250 calcium carbonate 150 clay 2.5 acrylic emulsion 2.5 alcohol ester 2.5 2.5 surfactant (Triton) Production process of gr-7m) 0.5 ammonia 22 and acrylic semi gloss emulsion enamel for internal use: (1) Prepare raw materials according to the paint formula; ( Paint knowledge how about Akzo Nobel Powder Coating Recommended introduction: powder coating is a kind of coating with different form from general coating, which is in powder form It is a new type of coating, because of its own advantages and more and more known by people Let's introduce Akzo Nobel Powder coating Akzo Nobel Powder coating is a cost-effective coating solution, which can be applied to different kinds of products After the treatment of static electricity and fire baking, a tough and durable coating surface will be formed, with the least impact on the environment Since the introduction of this technology, powder coating has been able to continue to maintain the Coatings home news: 1, acrylic semi gloss emulsion paint formula: raw material /kg water 217.8 preservative 2.4 propylene glycol 25.9 dispersant 11.5 defoamer 3.8 surfactant 1 (Triton N-57) 12- amino -2- methyl -1- propanol 1 titanium white 250 250 calcium carbonate 150 clay 2.5 acrylic emulsion 2.5 alcohol ester, 2.5 surfactant surfactant (Triton) Gr-7m) 0.5 ammonia 22 The production process of acrylic semi gloss emulsion enamel: (1) prepare raw materials according to the paint formula; (2) add water to the pull cylinder of the paint dispersion mixer, add propylene glycol, start the mixer (rotating speed: 300r / min), add propylene glycol, surfactant 1, dispersant, 2-amino-2-methyl-1-propanol and mix for more than 10min, and mix evenly; (3) Under stirring, titanium dioxide, calcium carbonate, clay and 1.9kg defoamer were added to mix for more than 10min to make it fully wetted and dispersed into slurry Increase the speed of mixer to over 1000r / min, and mix for 20 minutes; (4) reduce the speed after the fineness is qualified, add the remaining components, and mix evenly; (5) stop the machine, discharge the material, load the barrel, and put it into storage Home of coatings is specialized in coatings, diatom mud, paint coating, coating technology, fire retardant coating news and coating, diatom mud, paint coating, coating technology, fire retardant coating decoration knowledge and decoration renderings,