Coating process: production process of vinyl acetate dibutyl maleate copolymer emulsion

Core tips: 1 Formulation of vinyl acetate dibutyl maleate copolymer emulsion paint: The amount of coating material is /kg water 34.77 titanium white powder (Jin Hongshi type) 17.38 talcum powder (400 mesh) 8.8 ethylene glycol 2 phosphoric acid three butyl ester 0.09 six sodium phosphate sodium 0.3 0.3 hydroxymethyl cellulose 0.07 emulsifier OP-100.16 polymethacrylate sodium 0.04 benzene acetate mercury benzene rosin alcohol 0.04 vinyl acetate - maleic acid butyl ester copolymer emulsion 2 Production worker of vinyl acetate dibutyl maleate copolymer emulsion paint Application scope and advantages of roller ceramic coating Recommended introduction: the surface of ceramic rubber plate used for roller ceramic coating is cast into durable rubber plate by hundreds of independent small ceramic pieces Each ceramic piece has raised characteristics Under general conveyor belt pressure, thousands of unique cast bumps can produce positive traction, prevent slipping and extend the service life of conveyor belt roller At the same time, the bottom layer adopts high-quality rubber, which has strong elasticity and can play a good impact resistance role The scope of application of roller ceramic coating is one three six 83857180 (the same as V) 1 Roller coating in extremely harsh working environment 2 The belt joint is not suitable for fixing with iron buckle; 3 It is suitable for leather Home of coatings: 1 Formulation of vinyl acetate dibutyl maleate copolymer emulsion paint: The amount of coating material is /kg water 34.77 titanium white powder (Jin Hongshi type) 17.38 talcum powder (400 mesh) 8.8 ethylene glycol 2 phosphoric acid three butyl ester 0.09 six sodium phosphate sodium 0.3 hydroxymethyl cellulose 0.07 emulsifier OP-100.16 poly sodium methacrylate 0.04 benzene acetate mercury benzene rosin alcohol 0.04 vinyl acetate - maleic acid butyl butyrate copolymer emulsion, butyl acetate, butylene maleate copolymer emulsion The production process of rubber paint: (1) prepare raw materials according to the paint formula; (2) add water into the pull cylinder of the paint dispersion mixer, start the mixer (rotating speed: 300r / min), and slowly add titanium dioxide, talcum powder, glycol, tributyl phosphate, sodium hexametaphosphate, emulsifier, hydroxymethylcellulose, sodium polymethylacrylate and rosin alcohol in turn and mix evenly; (3) Adjust the rotating speed of the mixer to more than 1000r / min, and mix for 20 minutes; (4) test the fineness, reduce the speed after passing the test, add the remaining components, and mix evenly; (5) stop the machine, filter, discharge, load the barrel, and store in the warehouse Home of coatings is specialized in coatings, diatom mud, paint coating, coating technology, fire retardant coating news and coating, diatom mud, paint coating, coating technology, fire retardant coating decoration knowledge and decoration renderings,