Paint formula: a new type of water-based dry powder architectural paint formula

Key tips: 1 Formulation of new water-based dry powder architectural coating Raw material W / kg cellulose ether 2-5 dispersant 3-10 defoamer 3-5 pigment 150-200 filler ① 100-150 filler ② 100-150 dispersible latex powder 100-200 wood fiber 3-10 thixotropic lubricant appropriate amount of other additives during construction water addition 350-450 white paint formula, the color of titanium white powder In the colored coating, the ratio of M (titanium dioxide): m (iron oxide red) = 4:1 is used In order to obtain better covering power and stability, the filler is adopted Paint knowledge how about Akzo Nobel Powder Coating Recommended introduction: powder coating is a kind of coating with different form from general coating, which is in powder form It is a new type of coating, because of its own advantages and more and more known by people Let's introduce Akzo Nobel Powder coating Akzo Nobel Powder coating is a cost-effective coating solution, which can be applied to different kinds of products After the treatment of static electricity and fire baking, a tough and durable coating surface will be formed, with the least impact on the environment Since the introduction of this technology, powder coating has been able to continue to maintain the Home of coatings: 1 Raw materials of new water-based dry powder building coatings: w / kg cellulose ether 2-5 dispersant 3-10 defoamer 3-5 pigment 150-200 filler ① 100-150 filler ② 100-150 dispersible latex powder 100-200 wood fiber 3-10 thixotropic lubricant proper amount of other additives proper amount of water added during construction 350-450 In the formula of white paint, titanium dioxide is used as the color In the colored coating, the ratio of M (titanium dioxide): m (iron oxide red) = 4:1 is used In order to obtain better covering power and stability, two different kinds of powder are used in the packing 2 Before construction, part of the water shall be added into the container, and then the powder shall be added slowly The mixing speed shall be controlled at 750r / min (close to the speed of the electric mixer on site) Considering the actual situation of construction, the mixing time shall be controlled at 15min, and then the remaining water shall be added to adjust to the appropriate viscosity (the paint formula in this paper is for reference only) paint home is focused on the news and information of coating, diatom mud, paint coating, coating process, fire retardant coating, and coating, diatom mud, paint coating, coating process, decoration knowledge and decoration effect map of fire retardant coating,