    Research progress of waterborne polyurethane blending modification!

    • Last Update: 2022-01-21
    • Source: Internet
    • Author: User
    Search more information of high quality chemicals, good prices and reliable suppliers, visit www.echemi.com

    Although waterborne polyurethane has good environmental advantages, in order to make the PU prepolymer easy to emulsify in water, the molecular chain of waterborne polyurethane contains hydrophilic groups, such as carboxyl groups, hydroxyl groups,



    Blending modification, also known as physical modification, is a modification method in which the synthesized water-based polyurethane emulsion is mixed with different nanoparticles and resin materials through high-intensity mechanical stirring in different proportions.



    The aqueous polyurethane emulsion was synthesized by the acetone method, and then colloidal SiO2 with a content of 0-50wt% was added to the aqueous polyurethane emulsion, and a series of WPU/SiO2 mixed materials were obtained by vigorous stirring



    A waterborne polyurethane (referred to as P) was first synthesized with polydimethylsiloxane (PDMS) as the only soft segment, then P was mixed with different types of waterborne polyurethanes, and a small amount of P was used to study the mixed waterborne polyurethane emulsion Influence of properties, surface structure and properties of membranes



    Ethyl orthosilicate (TEOS) was directly added to amino-terminated PU resin to prepare WPU/SiO2 hybrid materials



    3 wt% TEOS was added dropwise to the aqueous polyurethane emulsion, and the WPU/SiO2 hybrid material was synthesized by the sol-gel method



    Firstly, the surface of fumed SiO2 and nano-SiO2 in silica sol was chemically grafted and modified, and then the modified nano-SiO2 particles were added to the synthesized water-based polyurethane emulsion to prepare a series of nano-SiO2 blends with different contents.



    Add the epoxy resin E-51 diluted with acetone into the water-based polyurethane emulsion, and disperse at high speed to make it evenly mixed



    The blending modification has the advantages of low cost, easy operation, convenient formula ratio adjustment, and can be used as needed
    .
    However, in the blending modification, the interaction between the modified particles and PU is weak, no substantial chemical bonds are formed, and the degree of phase separation is high
    .
    Moreover, the nanoparticles in the mixed system obtained by the blending method are prone to agglomeration, the product uniformity is not good, and it is difficult to obtain high-performance waterborne polyurethane products
    .


    This article is an English version of an article which is originally in the Chinese language on echemi.com and is provided for information purposes only. This website makes no representation or warranty of any kind, either expressed or implied, as to the accuracy, completeness ownership or reliability of the article or any translations thereof. If you have any concerns or complaints relating to the article, please send an email, providing a detailed description of the concern or complaint, to service@echemi.com. A staff member will contact you within 5 working days. Once verified, infringing content will be removed immediately.