Coating formula: flame retardant coating

Core tips: 1 CYC type facing flame retardant coating Flame retardant coating is a kind of coating which can be applied on the surface of the object, block the flame spread, extend the ignition time of the base material or improve the heat insulation performance to delay the damage time of the structure (1) Paint formulation Composition dosage /% chlorine partial emulsion 23~33 ammonium polyphosphate 20~30 melamine 10.5 to 15.5 pentaerythritol 12~17 titanium white powder 7 dispersant 0.5 emulsion stabilizer 0.3 chlorinated paraffin 3.2 dibutyl phthalate 3 smoke suppressant 7 water 7 process Configuration assistance Paint knowledge how about Akzo Nobel Powder Coating Recommended introduction: powder coating is a kind of coating with different form from general coating, which is in powder form It is a new type of coating, because of its own advantages and more and more known by people Let's introduce Akzo Nobel Powder coating Akzo Nobel Powder coating is a cost-effective coating solution, which can be applied to different kinds of products After the treatment of static electricity and fire baking, a tough and durable coating surface will be formed, with the least impact on the environment Since the introduction of this technology, powder coating has been able to continue to maintain the Coatings home news: 1 CYC type flame retardant coating is a kind of coating which can be applied on the surface of the object, block the flame spread, extend the ignition time of the base material or improve the thermal insulation performance to delay the damage time of the structure It belongs to special coating (1) coating formulation ingredients dosage /% chlorine partial emulsion 23~33 ammonium phosphate 20~30 melamine 10.5 to 15.5 pentaerythritol 12~17 titanium white powder 7 dispersant 0.5 emulsion stabilizer 0.3 chlorinated paraffin 3.2 dibutyl phthalate 3 smoke suppressant 3.2 water production process configuration auxiliaries solution and coloring pigment Pulverized materials and water are dispersed into sand slurry mills and ball mills to form a resistance fuel slurry The emulsion, flame retardant slurry, auxiliaries and color paste are modulated into flame retardant coatings in the paint cylinder and tested and packed The coating is non-toxic, non irritating, non combustible and non explosive The product is a single component and can be applied after being stirred evenly The construction needs to be carried out in the environment with temperature higher than 4 ℃, relative humidity lower than 90% and air circulation to ensure the normal drying and curing of the film When it is used on the surface of combustible base materials of buildings, it shall be measured as 500g / ㎡, generally 3 coats, once every 4 hours 2 Forest water-based fire retardant coating this fire retardant coating can be used for the fire protection of trees in the growing period He brushed on the trunk of the trees, which did not affect the normal growth of the trees, and played a role in fire prevention in case of forest fire The preparation method is to prepare hydroxyethyl cellulose in 1% water solution, then mix it with phosphate, melamine, pentaerythritol, chlorinated paraffin, titanium dioxide and talcum powder, tap water with high speed dispersing machine, stir 20 ~ 60min, and then grind it through the lapping machine, then mix the water base resin / emulsion, stir, filter and test Coating formula: component mass: polyphosphate amine 20 melamine 9 pentaerythritol 6 oxidized paraffin 5 titanium dioxide 5 talcum powder 4 hydroxyethyl cellulose 0.6 tap water 20 water-based acrylic resin 30 (formula in this paper is for reference only) coating house is focused on coating, diatom mud, paint coating, coating technology, fire retardant coating news and coating, diatom mud, paint coating, Coating technology, decoration knowledge and decoration effect drawing of fireproof coating,